- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 2.2
- 拉伸強(qiáng)度 [MPa]: 43.0
- 熱變形溫度 [℃]: 155.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption | 2.2 % @Temperature 23.0 °C | 2.2 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 7.0 % @Temperature 23.0 °C | 7.0 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage | 0.015 cm/cm @Thickness 3.20 mm | 0.015 in/in @Thickness 0.126 in | Flow; DAM | ||
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Thickness 2.00 mm | 0.015 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Thickness 2.00 mm | 0.015 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 43.0 MPa @Temperature 23.0 °C | 6240 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 61.0 MPa @Temperature 23.0 °C | 8850 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 35 % @Temperature 23.0 °C | 35 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| Elongation at Yield | 6.0 % @Temperature 23.0 °C | 6.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 26 % @Temperature 23.0 °C | 26 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.10 GPa @Temperature 23.0 °C | 160 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 2.20 GPa @Temperature 23.0 °C | 319 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.800 J/cm2 @Temperature -30.0 °C | 3.81 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 1.50 J/cm2 @Temperature -30.0 °C | 7.14 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 1.50 J/cm2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 2.50 J/cm2 @Temperature 23.0 °C | 11.9 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 132 μm/m-°C @Temperature 23.0 - 55.0 °C | 73.3 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Features | Food Contact Acceptable | DAM | |||
| Impact Modified | DAM | ||||
| Impact Modified | DAM | ||||
| Lubricated | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-I< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Food Contact Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Unreinforced Resins | DAM | ||||
| Resin Identification | PA66-I | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Food Applications, Non-specific | DAM | |||