- 吸水率 [%]: 1.2
- 缺口沖擊強度: 8.0
- 拉伸強度 [MPa]: 50.0
- 彎曲模量 [MPa]: 1.655
- 硬度: 119.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Water Absorption | 1.2 % @Time 86400 sec | 1.2 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage | 0.016 cm/cm @Thickness 3.17 mm | 0.016 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 50 - 60 % | 50 - 60 % | ASTM D638 |
| Flexural Strength | 61.0 MPa | 8850 psi | ASTM D790 |
| Flexural Modulus | 1.655 GPa | 240.0 ksi | ASTM D790 |
| Izod Impact, Notched | 8.00 - 9.00 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 15.0 - 16.9 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| NB @Thickness 3.17 mm, Temperature -40.0 °C | NB @Thickness 0.125 in, Temperature -40.0 °F | ASTM D256 | |
| Izod Impact, Unnotched | 133 - 160 J/cm @Thickness 3.17 mm | 249 - 300 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ASTM D648 |