- 密度 [g/cm3]: 1.29
- 吸水率 [%]: 0.9
- 缺口沖擊強度: 0.8
- 彎曲強度 [MPa]: 124.0
- 彎曲模量 [MPa]: 7.60
- 硬度: 121.0
- 熱變形溫度 [℃]: 249.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in3 | ASTM D792 |
| Water Absorption | 0.90 % | 0.90 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 96 | 96 | ASTM D785 |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Ultimate | 124 MPa | 18000 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 214 MPa | 31000 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Compressive Yield Strength | 207 MPa | 30000 psi | ASTM D695 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 263 °C | 505 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 249 °C | >= 480 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |