- 密度 [g/cm3]: 1.26
- 吸水率 [%]: 0.5
- 缺口沖擊強度: 1.2
- 彎曲強度 [MPa]: 110.0
- 彎曲模量 [MPa]: 5.50
- 硬度: 120.0
- 熱變形溫度 [℃]: 249.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in3 | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 89 | 89 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
| Flexural Modulus | 5.50 GPa | 798 ksi | ASTM D790 |
| Compressive Yield Strength | 152 MPa | 22000 psi | ASTM D695 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 °C | 491 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 249 °C | 480 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |