- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.6
- 缺口沖擊強度: 0.3
- 彎曲強度 [MPa]: 138.0
- 彎曲模量 [MPa]: 7.60
- 硬度: 122.0
- 熱變形溫度 [℃]: 249.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in3 | ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 98 | 98 | ASTM D785 |
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Compressive Yield Strength | 255 MPa | 37000 psi | ASTM D695 |
| Izod Impact, Notched | 0.300 J/cm | 0.562 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 263 °C | 505 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 249 °C | 480 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |