- 密度 [g/cm3]: 1.43
- 彎曲模量 [MPa]: 44.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | |||
| Filler Content | 45 % | 45 % | by volume | ||
| Thickness | 250 microns | 9.84 mil | laminate layer thickness | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 725 MPa | 105000 psi | transverse; ISO 527-4/5 | ||
| 785 MPa | 114000 psi | longitudinal; ISO 527-4/5 | |||
| Elongation at Break | 2.1 % | 2.1 % | longitudinal; ISO 527-4/5 | ||
| 2.1 % | 2.1 % | transverse; ISO 527-4/5 | |||
| Tensile Modulus | 51.0 GPa | 7400 ksi | transverse; ISO 527-4/5 | ||
| 53.0 GPa | 7690 ksi | longitudinal; ISO 527-4/5 | |||
| Flexural Strength | 730 MPa | 106000 psi | transverse; ISO 178 | ||
| 760 MPa | 110000 psi | longitudinal; ISO 178 | |||
| Flexural Modulus | 44.1 GPa | 6400 ksi | transverse; ISO 178 | ||
| 45.5 GPa | 6600 ksi | longitudinal; ISO 178 | |||
| Poissons Ratio | 0.070 | 0.070 | longitudinal; ISO 527-4/5 | ||
| 0.070 | 0.070 | transverse; ISO 527-4/5 | |||
| Charpy Impact Unnotched | 11.0 J/cm2 @Temperature 23.0 °C | 52.3 ft-lb/in2 @Temperature 73.4 °F | longitudinal; ISO 179/1eU | ||
| 15.0 J/cm2 @Temperature -30.0 °C | 71.4 ft-lb/in2 @Temperature -22.0 °F | longitudinal; ISO 179/1eU | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | DSC 3146 | ||
| Maximum Service Temperature, Air | 130 °C @Time 7.20e+7 sec | 266 °F @Time 20000 hour | Relative Temperature Index; IEC 216/1 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-1/2 | ||
| Minimum Service Temperature, Air | -30.0 °C | -22.0 °F | |||
| Glass Transition Temp, Tg | 70.0 °C | 158 °F | DSC 3146 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 280 - 300 °C | 536 - 572 °F | |||
| Descriptive Properties | |||||
| Reinforcement | Area weight | 200 g/m2 | |||
| Fabric | twill 2/2 | ||||
| Fibers | carbon | ||||
| Weight Rate | 50% longitudinal and transverse | ||||
| Yarn | 3000 tex longitudinal and transverse | ||||