- 密度 [g/cm3]: 1.18
- 缺口沖擊強度: 14.0
- 彎曲模量 [MPa]: 4.40
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 | ||
| Elongation at Break | 4.1 % | 4.1 % | ISO 527 | ||
| Tensile Modulus | 4.90 GPa | 711 ksi | ISO 527 | ||
| Flexural Modulus | 4.40 GPa | 638 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 14.0 kJ/m2 | 6.66 ft-lb/in2 | ISO 180 | ||
| Charpy Impact, Notched | 1.40 J/cm2 | 6.66 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 288 - 305 °C | 550 - 581 °F | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Dry Time | 1 - 2 hour | 1 - 2 hour | |||
| Injection Pressure | 35.0 - 125 MPa | 5080 - 18100 psi | |||
| Back Pressure | 0.000 - 0.350 MPa | 0.000 - 50.8 psi | |||
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | |||
| Descriptive Properties | |||||
| Color | BK 20465 | ||||
| Commercial Status | North America | ||||