- 熔體流動速率 [g/10min]: 157.2
- 密度 [g/cm3]: 1.31
- 拉伸強度 [MPa]: 50.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in3 | |||
| Density | 1.31 g/cc | 0.0473 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 2.0 - 2.4 % | 2.0 - 2.4 % | 23°C; 50% RH; ISO 62 | ||
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | |||
| Melt Flow | 157.2 g/10 min @Load 5.00 kg, Temperature 275 °C | 157.2 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 11.0 J/cm2 @Temperature 23.0 °C | 52.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Hot Wire Ignition, HWI | 2.0 sec @Thickness >=1.50 mm | 2.0 sec @Thickness >=0.0591 in | ASTM D3874-88 | ||
| High Amp Arc Ignition, HAI | 0.00 arcs @Thickness >=0.700 mm | 0.00 arcs @Thickness >=0.0276 in | UL 746C | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | >= 90.0 μm/m-°C | >= 50.0 μin/in-°F | |||
| Melting Point | 220 °C | 428 °F | ISO 3146 | ||
| Decomposition Temperature | >= 300 °C | >= 572 °F | |||
| UL RTI, Electrical | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | ||
| Oxygen Index | 29 % | 29 % | Limiting; ISO 4589-2 | ||
| Glow Wire Test | 960 °C @Thickness 1.00 mm | 1760 °F @Thickness 0.0394 in | IEC 60695-2-12 | ||
| Descriptive Properties | |||||
| Color | Grey 22985 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >350°C | ASTM D1929 | |||