- 密度 [g/cm3]: 1.08
- 缺口沖擊強度: 22.0
- 拉伸強度 [MPa]: 46.0
- 彎曲模量 [MPa]: 1.703
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | ISO 527 | ||
| Elongation at Break | 50 % | 50 % | Nominal; ISO 527 | ||
| Flexural Modulus | 1.703 GPa | 247.0 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 22.0 kJ/m2 @Temperature -40.0 °C | 10.5 ft-lb/in2 @Temperature -40.0 °F | ISO 180 | ||
| 83.0 kJ/m2 @Temperature 23.0 °C | 39.5 ft-lb/in2 @Temperature 73.4 °F | ISO 180 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 258 °C | 496 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 304 °C | 536 - 579 °F | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | >= 0.20 % | >= 0.20 % | |||
| Injection Pressure | 35.0 - 125 MPa | 5080 - 18100 psi | |||
| Back Pressure | 0.000 - 0.350 MPa | 0.000 - 50.8 psi | |||
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | |||
| Descriptive Properties | |||||
| Color | BK 23220 | ||||
| Commercial Status | North America | ||||