- 密度 [g/cm3]: 1.75
- 缺口沖擊強度: 12.0
- 彎曲模量 [MPa]: 18.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.75 g/cc | 0.0632 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 248 MPa | 36000 psi | ISO 527 | ||
| Elongation at Break | 2.2 % | 2.2 % | ISO 527 | ||
| Tensile Modulus | 20.2 GPa | 2930 ksi | ISO 527 | ||
| Flexural Strength | 383 MPa | 55500 psi | ISO 178 | ||
| Flexural Modulus | 18.9 GPa | 2740 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 | 5.71 ft-lb/in2 | ISO 180 | ||
| 13.0 kJ/m2 | 6.19 ft-lb/in2 | ISO 180 | |||
| Charpy Impact Unnotched | 9.50 J/cm2 @Temperature -30.0 °C | 45.2 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | ||
| 9.90 J/cm2 @Temperature 23.0 °C | 47.1 ft-lb/in2 @Temperature 73.4 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.20 J/cm2 @Temperature -30.0 °C | 5.71 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | ||
| 1.30 J/cm2 @Temperature 23.0 °C | 6.19 ft-lb/in2 @Temperature 73.4 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 305 °C | 536 - 581 °F | |||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.12 % | <= 0.12 % | |||
| Descriptive Properties | |||||
| Color | BK 102 | ||||
| Commercial Status | North America | ||||