| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength | 118 MPa @Temperature 120 °C | 17100 psi @Temperature 248 °F | |||
| Tensile Modulus | 7.335 GPa @Temperature 120 °C | 1064 ksi @Temperature 248 °F | |||
| Charpy Impact, Notched | 1.40 J/cm2 @Temperature -30.0 °C | 6.66 ft-lb/in2 @Temperature -22.0 °F | |||
| 3.50 J/cm2 @Temperature 23.0 °C | 16.7 ft-lb/in2 @Temperature 73.4 °F | Conditioned: 15 days, 70°C, 70% humidity | |||
| 3.70 J/cm2 @Temperature 23.0 °C | 17.6 ft-lb/in2 @Temperature 73.4 °F | ||||
| Dart Drop, Total Energy | 4.50 J @Temperature -30.0 °C | 3.32 ft-lb @Temperature -22.0 °F | |||
| 9.00 J @Temperature 23.0 °C | 6.64 ft-lb @Temperature 73.4 °F | ||||
| Tensile Creep Modulus, 1000 hours | 40.0 MPa @Temperature 120 °C | 5800 psi @Temperature 248 °F | |||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||
| Continuous Vibration Test Cycles | 70 Mpa | R= -1 | |||
| Creep Elongation | 0.4 | 1 hr @ 40 Mpa, 120°C, | |||
| 0.43 | 1 hr @ 40 Mpa, 150°C, | ||||
| 0.5 | 100 hr @ 40 Mpa, 120°C, | ||||
| 0.5 | 100 hr @ 40 Mpa, 150°C, | ||||
| 0.54 | 1000 hr @ 40 Mpa, 120°C, | ||||
| 0.55 | 1000 hr @ 40 Mpa, 150°C, | ||||