- 熔體流動速率 [g/10min]: 131.0
- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 6.6
- 缺口沖擊強度: 6.0
- 拉伸強度 [MPa]: 40.0
- 彎曲模量 [MPa]: 2.80
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in3 | ISO 1183 | ||
| Water Absorption | 6.6 - 7.2 % | 6.6 - 7.2 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.0 - 2.4 % | 2.0 - 2.4 % | 23°C; 50% RH; ISO 62 | ||
| Melt Flow | 131 g/10 min @Load 5.00 kg, Temperature 275 °C | 131 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 2.90 GPa | 421 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 5.00 J/cm2 @Temperature 23.0 °C | 23.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.600 J/cm2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Comparative Tracking Index | 525 V | 525 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | >= 90.0 μm/m-°C | >= 50.0 μin/in-°F | |||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||