- 熔體流動速率 [g/10min]: 34.75
- 密度 [g/cm3]: 1.39
- 彎曲模量 [MPa]: 9.50
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in3 | |||
| Density | 1.39 g/cc | 0.0502 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 1.1 - 1.5 % | 1.1 - 1.5 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |||
| Melt Flow | 34.75 g/10 min @Load 5.00 kg, Temperature 275 °C | 34.75 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 | ||
| Modulus of Elasticity | 9.50 GPa | 1380 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 230 MPa | 33400 psi | ISO 178 | ||
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 6.30 J/cm2 @Temperature -30.0 °C | 30.0 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 6.50 J/cm2 @Temperature 23.0 °C | 30.9 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.750 J/cm2 @Temperature 23.0 °C | 3.57 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz | 3.8 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.017 @Frequency 1.00e+6 Hz | 0.017 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 | ||
| Hot Wire Ignition, HWI | 0.00 sec @Thickness >=0.750 mm | 0.00 sec @Thickness >=0.0295 in | ASTM D 3874-88 | ||
| High Amp Arc Ignition, HAI | 0.00 arcs @Thickness >=0.750 mm | 0.00 arcs @Thickness >=0.0295 in | US 746C | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 527-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 527-1/-2 | ||
| Decomposition Temperature | >= 310 °C | >= 590 °F | |||
| UL RTI, Electrical | 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | UL-746B | ||
| Flammability, UL94 | V-0 @Thickness >=0.750 mm | V-0 @Thickness >=0.0295 in | |||
| Oxygen Index | 32 % | 32 % | Limiting; ISO 4589-1/-2 | ||
| Glow Wire Test | 960 °C @Thickness 1.00 mm | 1760 °F @Thickness 0.0394 in | IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding/Extrusion | ||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Injection Molding | ||
| Descriptive Properties | |||||
| Color | BK 23260 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >350°C | ASTM D1929 | |||