- 熔體流動速率 [g/10min]: 66.0
- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 5.7
- 缺口沖擊強度: 15.0
- 彎曲模量 [MPa]: 6.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in3 | |||
| Density | 1.32 g/cc | 0.0477 lb/in3 | ISO 1183 | ||
| Water Absorption | 5.7 - 6.3 % | 5.7 - 6.3 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.7 - 2.1 % | 1.7 - 2.1 % | ISO 62 | ||
| Viscosity Measurement | 145 | 145 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | |||
| Melt Flow | 66 g/10 min @Load 5.00 kg, Temperature 275 °C | 66 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 | ||
| Elongation at Break | 6.0 % | 6.0 % | ISO 527-1/-2 | ||
| Modulus of Elasticity | 6.50 GPa | 943 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 | ||
| Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 15.0 kJ/m2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | ||
| Charpy Impact Unnotched | 9.00 J/cm2 @Temperature 23.0 °C | 42.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.80 J/cm2 @Temperature 23.0 °C | 8.57 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 5.5 @Frequency 1.00e+6 Hz | 5.5 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.16 @Frequency 1.00e+6 Hz | 0.16 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft2-°F | DIN 52612-1 | ||
| Melting Point | 260 °C | 500 °F | ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 140 °C | 284 °F | for 50% loss of tensile strength after 5000hr | ||
| 170 °C | 338 °F | for 50% loss of tensile strength after 20000hr | |||
| 240 °C | 464 °F | ||||
| Decomposition Temperature | >= 310 °C | >= 590 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding | ||
| Descriptive Properties | |||||
| Color | BK 23189 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D1929 | |||