- 熔體流動速率 [g/10min]: 40.0
- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 3.7
- 缺口沖擊強度: 14.0
- 拉伸強度 [MPa]: 180.0
- 彎曲模量 [MPa]: 13.0
- 熱變形溫度 [℃]: 250.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in3 | ISO 1183 | ||
| Water Absorption | 3.7 - 4.3 % | 3.7 - 4.3 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.70 - 1.1 % | 0.70 - 1.1 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 140 | 140 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | restricted | ||
| Melt Flow | 40 g/10 min @Load 5.00 kg, Temperature 275 °C | 40 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 180 MPa | 26100 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 2.0 % | 2.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 16.0 GPa | 2320 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 13.0 GPa | 1890 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 14.0 kJ/m2 @Temperature 23.0 °C | 6.66 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 5.00 J/cm2 @Temperature -30.0 °C | 23.8 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 5.50 J/cm2 @Temperature 23.0 °C | 26.2 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.10 J/cm2 @Temperature -30.0 °C | 5.23 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.30 J/cm2 @Temperature 23.0 °C | 6.19 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.6 @Frequency 1.00 Hz | 3.6 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Hot Wire Ignition, HWI | 1.0 sec @Thickness >=0.800 mm | 1.0 sec @Thickness >=0.0315 in | ASTM D3874-88 | ||
| High Amp Arc Ignition, HAI | 1.0 arcs @Thickness >=0.800 mm | 1.0 arcs @Thickness >=0.0315 in | UL 746C | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 15.0 - 20.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 8.33 - 11.1 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 40.0 - 50.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 22.2 - 27.8 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |||
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 125 °C | 257 °F | for 50% loss of tensile strength after 20000hr | ||
| 145 °C | 293 °F | for 50% loss of tensile strength after 5000hr | |||
| 220 °C | 428 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 310 °C | >= 590 °F | |||
| UL RTI, Electrical | 115 °C @Thickness 1.50 mm | 239 °F @Thickness 0.0591 in | UL 746B | ||
| Flammability, UL94 | V-2 @Thickness >=0.800 mm | V-2 @Thickness >=0.0315 in | |||
| V-0 @Thickness >=1.50 mm | V-0 @Thickness >=0.0591 in | ||||
| Oxygen Index | 28 % | 28 % | Limiting; ISO 4589-2 | ||
| Glow Wire Test | 960 °C @Thickness 0.800 mm | 1760 °F @Thickness 0.0315 in | IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 295 °C | 563 °F | Feed Zone | ||
| Zone 2 | 295 °C | 563 °F | Compression | ||
| Zone 3 | 295 °C | 563 °F | Metering-zone | ||
| Zone 4 | 295 °C | 563 °F | Nozzle | ||
| Melt Temperature | 290 - 300 °C | 554 - 572 °F | Injection-molding/Extrusion | ||
| 295 °C | 563 °F | Optimal | |||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| 85.0 °C | 185 °F | Optimal | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Color | BK 23187 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >350°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||