- 熔體流動速率 [g/10min]: 131.0
- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 6.6
- 缺口沖擊強度: 3.0
- 拉伸強度 [MPa]: 90.0
- 彎曲模量 [MPa]: 5.70
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in3 | ISO 1183 | ||
| Water Absorption | 6.6 - 7.2 % | 6.6 - 7.2 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.0 - 2.4 % | 2.0 - 2.4 % | 23°C; 50% RH; ISO 62 | ||
| Melt Flow | 131 g/10 min @Load 5.00 kg, Temperature 275 °C | 131 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 2.8 % | 2.8 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 6.10 GPa | 885 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 5.70 GPa | 827 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 3.00 kJ/m2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | ISO 180/A | ||
| 3.50 kJ/m2 @Temperature 23.0 °C | 1.67 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | |||
| Charpy Impact Unnotched | 2.50 J/cm2 @Temperature -30.0 °C | 11.9 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 3.00 J/cm2 @Temperature 23.0 °C | 14.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.300 J/cm2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.350 J/cm2 @Temperature 23.0 °C | 1.67 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Comparative Tracking Index | 525 V | 525 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 50.0 - 55.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 27.8 - 30.6 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 50.0 - 60.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 27.8 - 33.3 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-2 @Thickness >=0.710 mm | V-2 @Thickness >=0.0280 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||