- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.9
- 拉伸強度 [MPa]: 80.0
- 彎曲模量 [MPa]: 2.85
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ASTM D792 |
| Water Absorption | 1.9 % | 1.9 % | 24h in H2O; sim. ISO 62 |
| Water Absorption at Saturation | 9.0 % | 9.0 % | sim. ISO 62 |
| Viscosity Measurement | 50 | 50 | relative viscosity (formic acid); ASTM D789 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | parallel; Nilit |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ASTM D638 |
| Flexural Strength | 115 MPa | 16700 psi | ASTM D790 |
| Flexural Modulus | 2.85 GPa | 413 ksi | ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | >= 600 V | >= 600 V | UL 746 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Vicat Softening Point | 225 °C | 437 °F | 49 N; ASTM D1525 |
| 245 °C | 473 °F | 9.8 N; ASTM D1525 | |