- 拉伸強度 [MPa]: 46.0
- 彎曲模量 [MPa]: 1.42
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Volatiles | <= 0.20 % | <= 0.20 % | 5 min/100°C, Thermobalance | ||
| Melt Index of Compound | 6.5 g/10 min @Load 10.0 kg, Temperature 230 °C | 6.5 g/10 min @Load 22.0 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 50mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 95 % | 95 % | ASTM D638 | ||
| Elongation at Yield | 12 % | 12 % | 50mm/min; ASTM D638 | ||
| Flexural Modulus | 1.42 GPa | 206 ksi | 2mm/min; ASTM D790 | ||
| Descriptive Properties | |||||
| Color | Opaque | ||||
| Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.