| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in3 | ISO 1183 | ||
| Water Absorption | <= 0.040 % | <= 0.040 % | 24 hr @ 23°C; ISO 62 (method 1) | ||
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| 24 g/10 min @Load 5.00 kg, Temperature 230 °C | 24 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 800 % | 800 % | 50mm/min; ASTM D638 | ||
| Flexural Modulus | 1.00 GPa | 145 ksi | 2mm/min; ASTM D790 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | 10 mA, after 2 min; ASTM D257 | ||
| Surface Resistivity per Square | >= 1.00e+14 ohm | >= 1.00e+14 ohm | < 1V after 2 min - 500 V; ASTM D257 | ||
| Dielectric Constant | 7.0 @Frequency 1e+6 Hz | 7.0 @Frequency 1e+6 Hz | ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 160 °C | 320 °F | ASTM D3418 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | >= 65 % @Thickness 3.00 mm | >= 65 % @Thickness 0.118 in | limiting (sheet); ASTM D2863 | ||
| Descriptive Properties | |||||
| Form | Granules | ||||