- 密度 [g/cm3]: 1.78
- 拉伸強度 [MPa]: 50.0
- 彎曲模量 [MPa]: 1.93
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in3 | ISO 1183 | ||
| Water Absorption | <= 0.040 % | <= 0.040 % | 24 hr @ 23°C; ISO 62 (method 1) | ||
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | |||
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| 24 g/10 min @Load 5.00 kg, Temperature 230 °C | 24 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 50mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 35 % | 35 % | 50mm/min; ASTM D638 | ||
| Elongation at Yield | 8.0 % | 8.0 % | 50mm/min; ASTM D638 | ||
| Flexural Modulus | 1.93 GPa | 280 ksi | 2mm/min; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 169 °C | 336 °F | ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | |||
| Oxygen Index | >= 44 % @Thickness 3.00 mm | >= 44 % @Thickness 0.118 in | limiting (sheet); ASTM D2863 | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||