- 熔體流動速率 [g/10min]: 4.0
- 拉伸強度 [MPa]: 46.0
- 彎曲模量 [MPa]: 1.67
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Melt Flow | 4.0 - 6.0 g/10 min @Load 10.0 kg, Temperature 230 °C | 4.0 - 6.0 g/10 min @Load 22.0 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 67.0 MPa | 9720 psi | 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50 mm/min; ASTM D638 | ||
| Elongation at Break | 428 % | 428 % | 50 mm/min; ASTM D638 | ||
| Elongation at Yield | 9.0 % | 9.0 % | 50 mm/min; ASTM D638 | ||
| Flexural Modulus | 1.67 GPa | 242 ksi | 50 mm/min; ASTM D790 | ||
| Descriptive Properties | |||||
| Color | Opaque | ||||
| Volatile Matter | <0.2% | 5 min/110°, Thermobalance | |||