- 密度 [g/cm3]: 1.78
- 拉伸強度 [MPa]: 55.0
- 彎曲模量 [MPa]: 2.10
- 熱變形溫度 [℃]: 145.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in3 | ISO 1183 | ||
| Water Absorption | <= 0.040 % | <= 0.040 % | 24 hr @ 23°C; ISO 62 (method 1) | ||
| Melt Index of Compound | 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.50 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| 1.5 g/10 min @Load 5.00 kg, Temperature 230 °C | 1.5 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |||
| 5.0 g/10 min @Load 10.0 kg, Temperature 230 °C | 5.0 g/10 min @Load 22.0 lb, Temperature 446 °F | ASTM D1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 35 % | 35 % | ASTM D638 | ||
| Elongation at Yield | 7.0 % | 7.0 % | 50mm/min; ASTM D638 | ||
| Flexural Modulus | 2.10 GPa | 305 ksi | 2mm/min; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 174 °C | 345 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | >= 44 % @Thickness 3.00 mm | >= 44 % @Thickness 0.118 in | limiting (sheet); ASTM D2863 | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.