- 密度 [g/cm3]: 1.78
- 彎曲模量 [MPa]: 1.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in3 | ISO 1183 | ||
| Water Absorption | <= 0.040 % | <= 0.040 % | 24 hr @ 23°C; ISO 62 (method 1) | ||
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| 24 g/10 min @Load 5.00 kg, Temperature 230 °C | 24 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 600 % | 600 % | 50mm/min; ASTM D638 | ||
| Flexural Modulus | 1.00 GPa | 145 ksi | 2mm/min; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 160 °C | 320 °F | Crystallinity by DSC; ASTM D3418 | ||
| Descriptive Properties | |||||
| Form | Granules | ||||