- 熔體流動速率 [g/10min]: 0.9
- 缺口沖擊強(qiáng)度: 5.61
- 拉伸強(qiáng)度 [MPa]: 27.6
- 彎曲模量 [MPa]: 0.738
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.935 g/cc | 0.935 g/cc | ASTM D792 |
| ESCR 100% Igepal? | >= 1000 hour | >= 1000 hour | F50; ASTM D1693, B |
| ESCR 10% Igepal? | >= 1000 hour | >= 1000 hour | F50; ASTM D1693, B |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 25 g/10 min @Load 21.6 kg, Temperature 190 °C | 25 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 0.738 GPa | 107 ksi | ASTM D790 |
| Izod Impact, Notched | 5.61 J/cm | 10.5 ft-lb/in | ASTM D256 |
| Impact Test | 31.2 J @Temperature -20.0 °C | 23.0 ft-lb @Temperature -4.00 °F | Cold Temperature Impact Energy; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | ASTM D3417 |
| Optical Properties | Metric | English | Comments |
| Gloss | 40 - 80 % | 40 - 80 % | at 60°; TOTAL Method |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | Extrusion |