- 熔體流動速率 [g/10min]: 4.0
- 拉伸強度 [MPa]: 21.0
- 彎曲模量 [MPa]: 0.730
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.940 g/cc | 0.940 g/cc | ISO 1183 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133/D |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 21.0 MPa | 3050 psi | ISO 527-2 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ISO 527-2 |
| Elongation at Break | >= 800 % | >= 800 % | ISO 527-2 |
| Elongation at Yield | 11 % | 11 % | ISO 527-2 |
| Flexural Modulus | 0.730 GPa | 106 ksi | ISO 178 |
| Charpy Impact, Notched | >= 15.0 J/cm2 @Temperature 23.0 °C | >= 71.4 ft-lb/in2 @Temperature 73.4 °F | ISO 179-1 |
| >= 15.0 J/cm2 @Temperature -30.0 °C | >= 71.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179-1 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | ISO 11357 |