- 熔體流動速率 [g/10min]: 4.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.940 g/cc | 0.940 g/cc | ISO 1183 |
| Thickness | 20.0 microns | 0.787 mil | |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 14.5 MPa | 2100 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 14.7 MPa | 2130 psi | ISO 527-3 |
| Film Elongation at Break, MD | 480 % | 480 % | ISO 527-3 |
| Film Elongation at Break, TD | 610 % | 610 % | ISO 527-3 |
| Elmendorf Tear Strength, MD | 1.10 g/micron | 27.9 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 9.20 g/micron | 234 g/mil | ISO 6383-2 |
| Dart drop Test | 30.0 g | 0.0662 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 33.0 MPa | 4790 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 26.0 MPa | 3770 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | ISO 11357 |
| Vicat Softening Point | 122 °C | 252 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.5 % | 5.5 % | ISO 14782 |
| Gloss | 86 % | 86 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 60.0 °C | 68.0 - 140 °F | Chill Roll |
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |