- 熔體流動速率 [g/10min]: 0.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.927 g/cc | 0.927 g/cc | ISO 1183 |
| Water Vapor Transmission | 14.0 g/m2/day | 0.900 g/100 in2/day | ASTM E96/66 |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 30 g/10 min @Load 21.6 kg, Temperature 190 °C | 30 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 580 % | 580 % | ASTM D882, A |
| Film Elongation at Break, TD | 720 % | 720 % | ASTM D882, A |
| Coefficient of Friction | 0.50 | 0.50 | I/I; Total Method |
| Elmendorf Tear Strength MD | 165 g | 165 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 500 g | 500 g | ASTM D1922 |
| Dart drop Test | 150 g | 0.331 lb | ASTM D1709, A |
| Film Tensile Strength at Break, MD | 33.8 MPa | 4900 psi | ASTM D882, A |
| Film Tensile Strength at Break, TD | 33.1 MPa | 4800 psi | ASTM D882, A |
| 1% Secant Modulus, MD | 214 MPa | 31000 psi | ASTM D882, A |
| 1% Secant Modulus, TD | 172 MPa | 25000 psi | ASTM D882, A |
| Heat Seal Strength Initiation Temperature | 112 °C | 234 °F | Total Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 121 °C | 250 °F | ASTM D3417 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 65 % | 65 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 193 - 210 °C | 380 - 410 °F | Extrusion |