- 熔體流動速率 [g/10min]: 5.2
- 密度 [g/cm3]: 0.932
- 拉伸強度 [MPa]: 15.9
- 彎曲模量 [MPa]: 0.503
- 熱變形溫度 [℃]: 49.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in3 | Exxon Method |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50, Condition B; ASTM D1693 |
| Melt Flow | 5.2 g/10 min | 5.2 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 15.9 MPa | 2310 psi | ASTM D638 |
| Elongation at Break | 765 % | 765 % | ASTM D638 |
| Flexural Modulus | 0.503 GPa | 73.0 ksi | ASTM D790 |
| Impact Test | 244 J @Thickness 6.35 mm, Temperature -40.0 °C | 180 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | Impact Strength; Max Force; ARM |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 125 °C | 257 °F | Exxon Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.0 °C | 98.6 °F | ASTM D648 |