- 密度 [g/cm3]: 0.935
- 拉伸強(qiáng)度 [MPa]: 16.0994
- 彎曲模量 [MPa]: 0.6000
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in3 | ASTM D1505 |
| Melt Index of Compound | 17 g/10 min @Load 2.16 kg, Temperature 190 °C | 17 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 | 52 | ASTM D2240 |
| Tensile Strength, Yield | 16.0994 MPa | 2335.02 psi | 2"/min; ASTM D638 |
| Elongation at Break | 361 % | 361 % | 2"/min; ASTM D638 |
| Flexural Modulus | 0.6000 GPa | 87.02 ksi | ASTM D790 |