- 熔體流動速率 [g/10min]: 0.057
- 密度 [g/cm3]: 0.949
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| Melt Flow | 0.057 g/10 min | 0.057 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 35.2 MPa | 5100 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 29.6 MPa | 4300 psi | ASTM D882 |
| Film Elongation at Break, MD | 360 % | 360 % | ASTM D882 |
| Film Elongation at Break, TD | 340 % | 340 % | ASTM D882 |
| Secant Modulus, MD | 0.938 GPa | 136 ksi | ASTM D882 |
| Secant Modulus, TD | 0.958 GPa | 139 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 14 g | 14 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 35 g | 35 g | ASTM D1922 |
| Dart drop Total Energy | 1070 J/cm | 2.00 ft-lb/mil | ASTM D4272 |
| Film Tensile Strength at Break, MD | 76.5 MPa | 11100 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 66.2 MPa | 9600 psi | ASTM D882 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 - 216 °C | 390 - 420 °F | |
| Die Opening | 0.1016 - 0.127 cm | 0.04000 - 0.0500 in | |
| Blow-up Ratio (BUR) | 3.5 - 4.5 | 3.5 - 4.5 | |