- 熔體流動速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.934
- 拉伸強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 0.600
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in3 | ISO 1183 | ||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | 10% ant.; ASTM D1693 | ||
| Melt Flow | 0.90 g/10 min @Load 2.16 kg | 0.90 g/10 min @Load 4.76 lb | ISO 1133 | ||
| 3.0 g/10 min @Load 5.00 kg | 3.0 g/10 min @Load 11.0 lb | ISO 1133 | |||
| High Load Melt Index | 25 g/10 min @Load 21.6 kg | 25 g/10 min @Load 47.6 lb | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 527 | ||
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO 527 | ||
| Elongation at Break | 860 % | 860 % | ISO 527 | ||
| Elongation at Yield | 12 % | 12 % | ISO 527 | ||
| Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D 790 | ||
| Dart drop Test | >= 50.0 g | >= 0.110 lb | 20μm; ASTM D 1709 | ||
| >= 100 g | >= 0.221 lb | 40μm; ASTM D 1709 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 124 °C | 255 °F | DSC | ||
| Vicat Softening Point | 122 °C | 252 °F | ISO 306 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 9.0 % | 9.0 % | 40μm; ASTM D 1003 | ||
| 10 % | 10 % | 20μm; ASTM D 1003 | |||
| Gloss | 50 % | 50 % | 45 degrees, 20μm; ASTM D 2457 | ||
| 61 % | 61 % | 45 degrees, 40μm; ASTM D 2457 | |||
| Descriptive Properties | |||||
| Food Status | This material is formulated to comply with most requirements of the food packaging regulations | ||||