- 熔體流動速率 [g/10min]: 0.65
- 密度 [g/cm3]: 0.945
- 拉伸強度 [MPa]: 16.5
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | Condition A - 10% Igepal?; ASTM D1693 |
| Absorption Coefficient | 450 | 450 | ASTM D3349 |
| Carbon Black Loading | 2.6 % | 2.6 % | |
| Melt Flow | 0.65 g/10 min | 0.65 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Tensile Strength, Yield | 16.5 MPa | 2400 psi | ASTM D638 |
| Elongation at Break | 880 % | 880 % | ASTM D638 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.55 @Frequency 1e+6 Hz | 2.55 @Frequency 1e+6 Hz | ASTM D1531 |
| Dielectric Strength | 21.7 kV/mm | 550 kV/in | DC; ASTM D149 |
| Dissipation Factor | 0.00050 @Frequency 1e+6 Hz | 0.00050 @Frequency 1e+6 Hz | ASTM D1531 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 175 μm/m-°C @Temperature 20.0 °C | 97.2 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 154 - 163 °C | 310 - 325 °F | |
| Zone 2 | 177 - 193 °C | 350 - 380 °F | |
| Zone 3 | 193 - 210 °C | 380 - 410 °F | |
| Zone 4-x | 204 - 218 °C | 400 - 425 °F | |
| Adapter Temperature | 204 - 218 °C | 400 - 425 °F | |
| Die Temperature | 204 - 218 °C | 400 - 425 °F | |