- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.935
- 缺口沖擊強度: 5.3
- 拉伸強度 [MPa]: 17.3
- 彎曲強度 [MPa]: 27.2
- 彎曲模量 [MPa]: 0.610
- 熱變形溫度 [℃]: 60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in3 | ASTM D792 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50, Condition A, ASTM D1693, 100% Igepal |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 27.2 MPa | 3950 psi | ASTM D638 |
| Tensile Strength, Yield | 17.3 MPa | 2510 psi | ASTM D638 |
| Elongation at Break | 1500 % | 1500 % | ASTM D638 |
| Elongation at Yield | 17.4 % | 17.4 % | ASTM D638 |
| Flexural Modulus | 0.610 GPa | 88.5 ksi | ASTM D790 |
| Izod Impact, Notched | 5.30 J/cm @Thickness 3.20 mm | 9.93 ft-lb/in @Thickness 0.126 in | ASTM D256 |
| Tensile Impact Strength | 163 kJ/m2 | 77.6 ft-lb/in2 | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 128 °C | 262 °F | ASTM D3417 |
| Crystallization Temperature | 112 °C | 234 °F | ASTM D3417 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D1525 |
| Vicat Softening Point | 113 °C | 235 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 204 - 315 °C | 399 - 599 °F | |