- 熔體流動速率 [g/10min]: 4.0
- 拉伸強度 [MPa]: 18.0
- 彎曲模量 [MPa]: 0.690
- 脆化溫度 [℃]: -70.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.936 g/cc | 0.936 g/cc | ISO 1183 |
| Environmental Stress Crack Resistance | >= 350 hour | >= 350 hour | ISO 22088 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 54 | 54 | ISO 868/A |
| Tensile Strength at Break | 21.0 MPa | 3050 psi | ISO 527 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527 |
| Elongation at Break | >= 700 % | >= 700 % | ISO 527 |
| Flexural Modulus | 0.690 GPa | 100 ksi | ISO 178 |
| Dart drop Total Energy | 220 J/cm | 0.412 ft-lb/mil | rotomolded sample; ISO 6603/2 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Internal method |
| Vicat Softening Point | 114 °C @Load 1.00 kg | 237 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |