- 熔體流動速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.938
- 缺口沖擊強度: 1.82
- 拉伸強度 [MPa]: 20.6
- 彎曲強度 [MPa]: 29.1
- 彎曲模量 [MPa]: 0.702
- 熱變形溫度 [℃]: 58.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | ASTM D792 |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Crystallinity | 56 % | 56 % | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 29.1 MPa | 4220 psi | ASTM D638 |
| Tensile Strength, Yield | 20.6 MPa | 2990 psi | ASTM D638 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Elongation at Yield | 12 % | 12 % | ASTM D638 |
| Flexural Modulus | 0.702 GPa | 102 ksi | ASTM D790 |
| Izod Impact, Notched | 1.82 J/cm @Thickness 3.20 mm | 3.41 ft-lb/in @Thickness 0.126 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 129 °C | 264 °F | ASTM D3417 |
| Crystallization Temperature | 114 °C | 237 °F | ASTM D3417 |
| Deflection Temperature at 0.46 MPa (66 psi) | 58.0 °C | 136 °F | ASTM D1525 |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |