- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.962
- 缺口沖擊強度: 1.18
- 拉伸強度 [MPa]: 29.4
- 彎曲強度 [MPa]: 34.3
- 彎曲模量 [MPa]: 1.03
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 600 hour | 600 hour | ASTM D1693 |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64 | 64 | ASTM D2240 |
| Tensile Strength, Ultimate | 34.3 MPa | 4980 psi | ASTM D638 |
| Tensile Strength, Yield | 29.4 MPa | 4270 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 1.03 GPa | 149 ksi | Olsen Stiffness; ASTM D747 |
| Izod Impact, Notched | 1.18 J/cm | 2.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 132 °C | 270 °F | ASTM D2117 |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |