- 熔體流動(dòng)速率 [g/10min]: 0.025
- 密度 [g/cm3]: 0.955
- 缺口沖擊強(qiáng)度: 4.9
- 拉伸強(qiáng)度 [MPa]: 34.3
- 彎曲強(qiáng)度 [MPa]: 42.2
- 彎曲模量 [MPa]: 0.981
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 1000 hour | 1000 hour | ASTM D1693 |
| Melt Flow | 0.025 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.025 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength, Ultimate | 42.2 MPa | 6120 psi | ASTM D638 |
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Flexural Modulus | 0.981 GPa | 142 ksi | Olsen Stiffness; ASTM D747 |
| Izod Impact, Notched | 4.90 J/cm | 9.18 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 131 °C | 268 °F | ASTM D2117 |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D1525 |
- 關(guān)鍵詞:
- HDPE
- 供應(yīng)
- Global B-8200 High Density Polyethylene