- 熔體流動速率 [g/10min]: 1.2
- 密度 [g/cm3]: 0.961
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.961 g/cc | 0.0347 lb/in3 | ASTM D 792 |
| Water Vapor Transmission | 9.31 g/m2/day | 0.600 g/100 in2/day | 100°F; E 96/66 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.2 g/10 min @Load 2.16 kg | 1.2 g/10 min @Load 4.76 lb | ASTM D 1238 |
| High Load Melt Index | 33 g/10 min @Load 21.6 kg | 33 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 26.2 MPa | 3800 psi | ASTM D 882 A |
| Film Tensile Strength at Yield, TD | >= 27.6 MPa | >= 4000 psi | ASTM D 882 A |
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D 882 A |
| Secant Modulus, MD | 0.689 GPa | 99.9 ksi | ASTM D 882 A |
| Secant Modulus, TD | 0.703 GPa | 102 ksi | ASTM D 882 A |
| Elmendorf Tear Strength MD | 24 g | 24 g | ASTM D 1922 |
| Elmendorf Tear Strength TD | 385 g | 385 g | ASTM D 1922 |
| Film Tensile Strength at Break, MD | >= 51.7 MPa | >= 7500 psi | ASTM D 882 A |
| Film Tensile Strength at Break, TD | >= 23.4 MPa | >= 3400 psi | ASTM D 882 A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 129 °C | 265 °F | ASTM D3417 |
| Optical Properties | Metric | English | Comments |
| Haze | 15 % | 15 % | ASTM D 1003 |
| Gloss | 50 % | 50 % | ASTM D 523 |