- 熔體流動速率 [g/10min]: 0.28
- 密度 [g/cm3]: 0.947
- 拉伸強度 [MPa]: 22.8
- 彎曲模量 [MPa]: 0.793
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.947 g/cc | 0.0342 lb/in3 | ASTM D 792 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | ASTM D1693 cond. C 100% lgepal |
| Melt Flow | 0.28 g/10 min @Load 2.16 kg | 0.28 g/10 min @Load 4.76 lb | ASTM D 1238 |
| High Load Melt Index | 20 g/10 min @Load 21.6 kg | 20 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM D 2240 |
| Tensile Strength, Yield | >= 22.8 MPa | >= 3300 psi | ASTM D 638 type IV |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D 638 type IV |
| Flexural Modulus | 0.793 GPa | 115 ksi | ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | ASTM D3417 |