- 密度 [g/cm3]: 0.939
- 拉伸強(qiáng)度 [MPa]: 17.9
- 彎曲模量 [MPa]: 0.703
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in3 | ASTM D 792 |
| High Load Melt Index | 20 g/10 min @Load 21.6 kg | 20 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| PENT | >= 5000 hour | >= 5000 hour | ASTM F 1473 |
| Hardness, Shore D | 65 | 65 | ASTM D 2240 |
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D 638 type IV |
| Tensile Strength, Yield | >= 17.9 MPa | >= 2600 psi | ASTM D 638 type IV |
| Elongation at Break | >= 700 % | >= 700 % | ASTM D 638 type IV |
| Flexural Modulus | 0.703 GPa | 102 ksi | ASTM D 790 |
| Hydrostatic Design Basis | 8.62 MPa | 1250 psi | Room Temperature; ASTM D 2837 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 216 μm/m-°C @Temperature 20.0 °C | 120 μin/in-°F @Temperature 68.0 °F | ASTM D 696 |
| Melting Point | 126 °C | 259 °F | ASTM D3417 |
| Vicat Softening Point | 127 °C | 260 °F | ISO 306 |