- 熔體流動速率 [g/10min]: 0.08
- 密度 [g/cm3]: 0.946
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in3 | ASTM D 792 |
| Water Vapor Transmission | 15.5 g/m2/day | 0.998 g/100 in2/day | 100°F; E 96/66 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.080 g/10 min @Load 2.16 kg | 0.080 g/10 min @Load 4.76 lb | ASTM D 1238 |
| 0.34 g/10 min @Load 5.00 kg | 0.34 g/10 min @Load 11.0 lb | ASTM D 1238 | |
| High Load Melt Index | 9.0 g/10 min @Load 21.6 kg | 9.0 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | >= 34.5 MPa | >= 5000 psi | ASTM D 882 A |
| Film Tensile Strength at Yield, TD | >= 33.1 MPa | >= 4800 psi | ASTM D 882 A |
| Film Elongation at Break, MD | 300 - 500 % | 300 - 500 % | ASTM D 882 A |
| Film Elongation at Break, TD | 300 - 500 % | 300 - 500 % | ASTM D 882 A |
| Secant Modulus, MD | 0.758 GPa | 110 ksi | ASTM D 882 A |
| Secant Modulus, TD | 0.841 GPa | 122 ksi | ASTM D 882 A |
| Elmendorf Tear Strength MD | 26 g | 26 g | ASTM D 1922 |
| Elmendorf Tear Strength TD | 120 g | 120 g | ASTM D 1922 |
| Dart drop Test | 350 g | 0.772 lb | ASTM D 1709 |
| Film Tensile Strength at Break, MD | >= 58.6 MPa | >= 8500 psi | ASTM D 882 A |
| Film Tensile Strength at Break, TD | >= 55.8 MPa | >= 8100 psi | ASTM D 882 A |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 258 °F | ASTM D3417 |