- 熔體流動速率 [g/10min]: 0.38
- 密度 [g/cm3]: 0.958
- 缺口沖擊強度: 4.27
- 拉伸強度 [MPa]: 22.8
- 彎曲模量 [MPa]: 0.862
- 熱變形溫度 [℃]: 77.8
- 脆化溫度 [℃]: -118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in3 | ASTM D 792 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | No failures, compressed ring, 25% Igepal; ASTM F 1248 |
| >= 5000 hour | >= 5000 hour | No failures; ASTM D 1693 cond. C | |
| Carbon Black Loading | 2.5 % | 2.5 % | ASTM D 1603 |
| Melt Flow | 0.38 g/10 min @Load 5.00 kg | 0.38 g/10 min @Load 11.0 lb | ASTM D 1238 |
| High Load Melt Index | 11 g/10 min @Load 21.6 kg | 11 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| PENT | >= 400 hour | >= 400 hour | ASTM F 1473 |
| Hardness, Shore D | 63 | 63 | ASTM D 2240 |
| Tensile Strength, Yield | >= 22.8 MPa | >= 3300 psi | ASTM D 638 type IV |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D 638 type IV |
| Flexural Modulus | 0.862 GPa | 125 ksi | ASTM D 790 |
| Secant Modulus | 0.793 GPa | 115 ksi | 2% Strain; ASTM D 638 type IV |
| Izod Impact, Notched | 4.27 J/cm @Thickness 3.17 mm | 8.00 ft-lb/in @Thickness 0.125 in | ASTM D256 A |
| Hydrostatic Design Basis | 11.0 MPa | 1600 psi | Room Temperature; ASTM D 2837 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 180 μm/m-°C @Temperature 20.0 °C | 100 μin/in-°F @Temperature 68.0 °F | ASTM D 696 |
| Melting Point | 126 °C | 258 °F | ASTM D3417 |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.8 °C | 172 °F | ASTM D 648 |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D 1525 |
| Brittleness Temperature | -118 °C | -180 °F | ASTM D 746 |