- 密度 [g/cm3]: 0.945
- 缺口沖擊強度: 5.34
- 拉伸強度 [MPa]: 24.8
- 彎曲模量 [MPa]: 1.17
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in3 | ASTM D 792 |
| Environmental Stress Crack Resistance | >= 700 hour | >= 700 hour | ASTM D1693 cond. B 100% lgepal |
| High Load Melt Index | 9.0 g/10 min @Load 21.6 kg | 9.0 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 24.8 MPa | >= 3600 psi | ASTM D 638 type IV |
| Elongation at Break | 650 % | 650 % | ASTM D 638, type IV |
| Flexural Modulus | 1.17 GPa | 170 ksi | ASTM D 790 |
| Izod Impact, Notched | 5.34 J/cm @Thickness 3.17 mm | 10.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |