- 熔體流動速率 [g/10min]: 0.045
- 密度 [g/cm3]: 0.952
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | Exxon Method |
| Thickness | 12.7 microns | 0.500 mil | |
| Melt Flow | 0.045 g/10 min | 0.045 g/10 min | Exxon Method (I2). HLMI (I21) is 8 g/10 min. |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 39.0 MPa | 5660 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 33.0 MPa | 4790 psi | ASTM D882 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 400 % | 400 % | ASTM D882 |
| Secant Modulus, MD | 0.965 GPa | 140 ksi | ASTM D882 |
| Secant Modulus, TD | 1.14 GPa | 165 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.591 g/micron | 15.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.15 g/micron | 80.0 g/mil | ASTM D1922 |
| Dart Drop | 24.6 g/micron | 625 g/mil | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 93.0 MPa | 13500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 72.0 MPa | 10400 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 129 °C | 264 °F | Exxon Method |