| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in3 | ASTM D 792 |
| Environmental Stress Crack Resistance | >= 600 hour | >= 600 hour | ASTM D1693 cond. B 100% lgepal |
| High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C | 12 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 26.2 MPa | >= 3800 psi | ASTM D 638 type IV |
| Elongation at Break | 600 % | 600 % | ASTM D 638, type IV |
| Flexural Modulus | 1.21 GPa | 175 ksi | ASTM D 790 |
| Izod Impact, Notched | 5.34 J/cm @Thickness 3.17 mm | 10.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 127 °C | 260 °F | ASTM D3417 |