- 熔體流動速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.952
- 拉伸強度 [MPa]: 26.9
- 彎曲模量 [MPa]: 1.31
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D 792 |
| Environmental Stress Crack Resistance | 50 hour | 50 hour | ASTM D1693 cond. B 10% lgepal |
| 100 hour | 100 hour | ASTM D1693 cond. B 100% lgepal | |
| Melt Flow | 0.35 g/10 min @Load 2.16 kg | 0.35 g/10 min @Load 4.76 lb | ASTM D 1238 |
| High Load Melt Index | 30 g/10 min @Load 21.6 kg | 30 g/10 min @Load 47.6 lb | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | >= 26.9 MPa | >= 3900 psi | ASTM D 638 type IV |
| Elongation at Break | 600 % | 600 % | ASTM D 638, type IV |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 128 °C | 263 °F | ASTM D3417 |