- 熔體流動速率 [g/10min]: 33.0
- 密度 [g/cm3]: 0.951
- 拉伸強度 [MPa]: 22.1
- 彎曲模量 [MPa]: 0.558
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in3 | ASTM D4883 |
| Environmental Stress Crack Resistance | <= 2.0 hour | <= 2.0 hour | F-50; 10% Igepal Cond. B; ASTM D-1693 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | Exxon Method |
| Melt Flow | 33 g/10 min @Load 2.16 kg, Temperature 190 °C | 33 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 55.8 cm | 22.0 in | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.1 MPa | 3210 psi | ASTM D638 |
| Elongation at Yield | 20 % | 20 % | ASTM D638 |
| Flexural Modulus | 0.558 GPa | 80.9 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 130 °C | 266 °F | Exxon Method |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 260 °C | 500 °F | Nozzle (Melt) |