- 熔體流動速率 [g/10min]: 6.7
- 密度 [g/cm3]: 0.952
- 拉伸強度 [MPa]: 24.1
- 彎曲模量 [MPa]: 0.662
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D4883 |
| Environmental Stress Crack Resistance | 9.0 hour | 9.0 hour | F-50; 10% Igepal Cond. B; ASTM D-1693 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | Exxon Method |
| Melt Flow | 6.7 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.7 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 36.0 cm | 14.2 in | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
| Elongation at Yield | 18 % | 18 % | ASTM D638 |
| Flexural Modulus | 0.662 GPa | 96.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 131 °C | 268 °F | Exxon Method |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 245 °C | 473 °F | Nozzle (Melt) |