- 熔體流動速率 [g/10min]: 4.5
- 密度 [g/cm3]: 0.954
- 拉伸強度 [MPa]: 24.8
- 彎曲模量 [MPa]: 0.676
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in3 | ASTM D4883 |
| Environmental Stress Crack Resistance | 16 hour | 16 hour | F-50; 10% Igepal Cond. B; ASTM D-1693 |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | Exxon Method |
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 33.0 cm | 13.0 in | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 24.8 MPa | 3600 psi | ASTM D638 |
| Elongation at Yield | 17 % | 17 % | ASTM D638 |
| Flexural Modulus | 0.676 GPa | 98.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 132 °C | 270 °F | Exxon Method |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 260 °C | 500 °F | Nozzle (Melt) |