- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.948
- 拉伸強度 [MPa]: 22.0
- 彎曲模量 [MPa]: 0.930
- 熱變形溫度 [℃]: 57.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in3 | Exxon Method |
| Environmental Stress Crack Resistance | 8.0 hour | 8.0 hour | F50, Condition B; ASTM D-1693 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 405 % | 405 % | ASTM D638 |
| Flexural Modulus | 0.930 GPa | 135 ksi | ASTM D790 |
| Impact Test | 203 J @Thickness 6.35 mm, Temperature -40.0 °C | 150 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | Impact Strength; Max Force; ARM |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 133 °C | 271 °F | Exxon Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 57.0 °C | 135 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ASTM D648 |